ABS韩国LG TR-558AI 透明蓝底清晰 高强度 高抗冲 电子电器

ABS韩国LGTR-558A1 物性认证数据表性能项目测试条件测试方法数值/描述单位机械性能拉伸强度(引张强度)ASTM D638/ISO 527430kg/cm?(MPa)[Lb/in2]断裂伸长率ASTM D638/ISO 52750%拉伸模量ASTM D638/ISO 52721200kg/cm?(MPa)[Lb/in2]拉伸屈服伸长率(延伸率)ASTM D638/ISO 527%拉伸断裂伸长率(延伸率)ASTM D638/ISO 527%弯曲模量(弯曲弹性率)ASTM D790/ISO 17820400kg/cm?(MPa)[Lb/in2]弯曲强度ASTM D790/ISO 178670kg/cm?(MPa)[Lb/in2]洛氏硬度ASTM D785105IZOD 缺口冲击强度1/4" 23℃ASTM D256/ISO 17915kg·cm/cm(J/M)ft·lb/in1/4" -30℃ASTM D256/ISO 179kg·cm/cm(J/M)ft·lb/in1/8" 23℃ASTM D256/ISO 179kg·cm/cm(J/M)ft·lb/in1/8" -30℃ASTM D256/ISO 179kg·cm/cm(J/M)ft·lb/inCharpy冲击强度23℃ （缺口）ASTM D256/ISO 179kg·cm/cm(J/M)ft·lb/in-30℃（缺口）ASTM D256/ISO 179kg·cm/cm(J/M)ft·lb/in23℃（无缺口）ASTM D256/ISO 179kg·cm/cm(J/M)ft·lb/in-30℃（无缺口）ASTM D256/ISO 179kg·cm/cm(J/M)ft·lb/in物性性能比重（密度）ASTM D792/ISO 11831.09成型收缩率ASTM D9550.4-0.7%熔融指数（流动系数）200℃/5kgASTM D1238/ISO 11332g/10min220℃/10kgASTM D1238/ISO 1133g/10min吸水率 23℃/24HASTM D570/ISO 62%热性能热变形温度退火ASTM D648/ISO 7586℃（℉）未退火ASTM D648/ISO 75℃（℉）维卡软化点ASTM D1525/ISO R30691℃（℉）熔点-℃（℉）燃烧性（率）UL94hb线性膨胀系数ASTM D696/ISO 11359mm/mm.℃加工条件干燥条件加工温度射嘴℃料筒前段℃料筒中段℃料筒后段℃熔体温度℃模具温度℃压力注塑压力Mpa保压压力Mpa背压Mpa螺杆转速rpm其他备注颜色特性用途供应食品级ABS塑胶原料食品级ABS PA-737台湾奇美PA-737高透明ABS PA-758台湾奇美PA- 758高透明ABS 920日本东丽920高透明ABSSX-200日本旭化成SX200高透明ABS TR-557韩国LG TR-577高透明ABSTR-558AI韩国LG TR-558AI高透明ABSTH-21日本电气化TH-21防火抗紫外线ABSFR15U美国GE FR15U防火ABS FR15U美国GE FR15防火抗紫外线ABSPA-764台湾奇美PA-764防火抗紫外线ABSPA-764B台湾奇美PA-764B防火ABS PA-765A台湾奇美PA-765A防火ABS PA-765A台湾奇美PA-765A耐高温ABS PA-777B台湾奇美PA-777B耐高温ABS PA-777D台湾奇美PA-777D耐高温ABS PA-777E台湾奇美PA-777E原料物性描述ABS 树脂是丙烯腈（A）-丁二烯（B）-乙烯（S）三种单体组分经接枝共聚而成的三元共聚物，由于三种单体在配比组合上的不同，将直接影响到ABS的多种性能，如丙烯腈含量的增加可起到改善ABS的耐油性和耐化学性能；丁二烯的增加可提高ABS的冲击韧性；而乙烯则可提供良好的成型加性能；因此，当今都利用这一点，并引入各种添加剂，生产出了牌号，性能用途各异的ABS，如通用级，抗冲级，高抗冲级，耐寒级，耐热级，阻燃级，增强级等品级的树脂.由于它具有综合机械性能优良，价格比较便宜，有良好刚性和尺寸稳定性，以及成型加工性能好等优点，在国民经济各个领域中得到了广泛的应用.典型应用范围汽车（仪表板，工具舱门，车轮盖，反光镜盒等），电冰箱，大强度工具（头发烘干机，搅拌器，食品加工机，割草机等），电话机壳体，打字机键盘，娱乐用车辆如高尔夫球手推车以及喷气式雪撬车,玩具等。